On the mechanism of inoculation of cast iron melts О механизме модифицирования чугунных рассплавов Върху механизма на модофицирането на чугунени стопилки CH. WANG H. FREDERIKSSON

---

In the present work the inoculation process has been studied. Particles of FeSi were added to a small cast iron melt. The dissolution was interrupted by quenching the melt. The samples were metallographically investigated and analyzed. During the dissolution process silicon carbide crystals and graphite particles were observed to form around the FeSi particles. It was also observed that these particles dissolved again shortly after the complete dissolution of the added FeSi particles. It was also shown that a locally high silicon and high carbon content existed for a long time after the dissolution process. Due to this inhomogenous distribution of silicon and carbon, homogenous nucleation of graphite occurs. The fading of inoculation can be explained by a homogenization of the uneven distribution of silicon and carbon. В докладываемой здесь работе изучен процесс модифицирования. К малому количеству чугунного расплава были прибавлены частицы FeSi. Растворение было прервано резким охлаждением расплава. Пробы исследовались и анализировались металлографически. Во время растворения наблюдалось образование кристаллов из карбида кремния и частиц графита около частиц FeSi. Замечалось также, что эти частицы растворяются снова вскоре после полного растворения добавленных частиц из FeSi. Было доказано также, что существует область с высоким содержанием кремния и углерода в течение долгого времени после приключения процесса растворения. Вследствии этого негомогенного распределения кремния и углерода получается гомогенное образование зародышей графита. Затухание модифицирования можно объяснить гомогенизированием неравномерного распределения кремния и углерода.